Parameter Table of One-Component Silicone, Deoxime Type
| Model |
Features |
Proportion 25℃ |
Dry time min/25℃ |
Hardness Shore |
Tensile strength MPa≥ |
Volume resistivity Ω•cm≥ |
Temperature |
| 2100T |
Flow-based coating
|
1.00±0.05 |
30 |
10±5 |
0.3 |
5.0×1014 |
-40～200 |
| 2101T |
Flowing
|
1.05±0.05 |
30 |
20±5 |
0.5 |
5.0×1014 |
-60～200 |
| 2102 |
Semi-flowing
|
1.05±0.05 |
30 |
20±5 |
0.8 |
5.0×1014 |
-60～200 |
| 2103 |
Semi-flowing
|
1.35±0.05 |
20 |
35±5 |
1.2 |
5.0×1014 |
-60～300 |
| 2105 |
Thixotropic
|
1.35±0.05 |
20 |
35±5 |
1.5 |
5.0×1014 |
-60～300 |
| 2106B\W |
Thixotropic
|
1.35±0.05 |
20 |
35±5 |
1.5 |
5.0×1014 |
-60～300 |
| 2106T |
Thixotropic
|
1.05±0.05 |
20 |
30±5 |
1.0 |
5.0×1014 |
-60～200 |
| 2108B |
Thixotropic
|
1.40±0.05 |
20 |
35±5 |
2.5 |
5.0×1014 |
-60～260 |
|
Directions for use:
|
1, the surface cleaning: remove with a clean cloth and solvent to be sizing of surface dust, oil, etc., so that clean and dry.
2, the sizing: the glue evenly pushed to the surface has been cleaned, parts assembly, proper positioning of the components stack merge.
3, the cure: the sealing components or assembled naturally cured in air. Curing outside to the inside, generally 24 hours curing depth of 2 ~ 4mm, 6mm sealant depth be fully cured more than 7 days, the temperature, high humidity is cured rapidly. When the glue has been solid early, and to ascertain follow-up without external damage, it can be under the procedures.
4, the operation is complete, unused plastic cap should be tightened immediately, kept under seal. Again, if the seal a little crust, its removal can not affect the normal use and performance. |
| Note: |
For bonding, potting when the depth of not more than 6mm; off oxime-type adhesive may be in the closed state of corrosion of copper and polycarbonate plastic, should be tested before use. |
|