Parameter Table of One-Component Silicone, Dealcoholized Type
| Model |
Features |
Proportion |
Dry time min/25℃ |
Hardness Shore A |
Tensile strength MPa≥ |
Volume resistivity Ω•cm≥ |
Temperature |
| 2201T |
Flow-based coating |
1.00±0.05 |
10 |
20±5 |
0.5 |
5.0×1014 |
-40～200 |
| 2203B\W |
Flow-based coating |
1.00±0.05 |
5 |
35±5 |
1.2 |
5.0×1014 |
-60～260 |
| 2206T |
Flow-based coating |
1.00±0.05 |
3 |
25±5 |
1.0 |
5.0×1014 |
-60～200 |
| 2206B\W |
Flow-based coating |
1.00±0.05 |
3 |
35±5 |
1.5 |
5.0×1014 |
-60～260 |
|
Directions for use:
|
1, the surface cleaning: remove with a clean cloth and solvent to be sizing of surface dust, oil, etc., so that clean and dry.
2, the sizing: the glue evenly pushed to the surface has been cleaned, parts assembly, proper positioning of the components stack merge.
3, the cure: the sealing components or assembled naturally cured in air. Curing outside to the inside, generally 24 hours curing depth of 2 ~ 4mm, 6mm sealant depth be fully cured more than 7 days, the temperature, high humidity is cured rapidly. When the glue has been solid early, and to ascertain follow-up without external damage, it can be under the procedures.
4, the operation is complete, unused plastic cap should be tightened immediately, kept under seal. Again, if the seal a little crust, its removal can not affect the normal use and performance. |
| Note: |
For bonding, potting when the depth of not more than 6mm; |
|